Mesh implant with an interlocking knitted structure

ABSTRACT

A resorbable polymeric mesh implant is provided for use in the reconstruction of soft tissue defects. The mesh implant is provided with an interlocking knitted structure comprising two or more sets of fibers with different times of degradation, allowing a stepwise increase in the relative distension of the overall mesh over time. The filamentous fibers are knitted together, wherein the filaments of the first set of fibers are interlaced into the filaments of the second set of fibers and at least partly traverse the knit pattern of the second set of fibers such that the filaments of the first set of fibers lock the movement of the part of the mesh formed by the second set of fibers.

CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. application Ser. No.11/808,563, filed Jun. 11, 2007, the entire contents of which isincorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to a resorbable polymeric mesh implantwith an interlocking knitted structure comprising two or more sets offibers with different times of degradation, allowing a stepwise increasein the relative distension of the overall mesh over time, intended to beused in the reconstruction of soft tissue defects.

BACKGROUND OF THE INVENTION

A hernia is an abnormal protrusion of a peritoneal-lined sac through themusculo-aponeurotic covering of the abdomen, the most common site for ahernia being the groin. Types of hernias are, among others, inguinalhernia or femoral hernia, hiatal hernia, umbilical hernia and incisionalhernia, the latter being a hernia that pushes through a past surgicalincision or operation site.

Hernias are repaired by a surgical procedure where the protrusion isretracted to its original position within the abdominal cavity, andsubsequent healing is facilitated by covering the abdominal wall defectwith a surgical implant. This can be done under local or generalanesthesia using a laparoscope or an open incision technique.

Within the field of surgical repair of soft tissue defects such ashernias, use is often made of a mesh implant fabricated of anon-resorbable material that is inserted to cover the area of the tissuedefect without sewing together the surrounding muscles. The mesh implantis used in order to support the regenerating tissue and works bymechanical closure of the defect as well as by inducing a strong scarfibrous tissue around the mesh implant. Such a mesh implant is mostoften made of various plastics, which are known to stay biostable andsafe for a number of years after implantation. However, measurements ofnine common mesh materials show a lower elasticity (with a mean value ofapproximately 15%) than that of the intact abdominal wall (23-32%) (K.Junge et al.: Elasticity of the anterior abdominal wall and impact forreparation of incisional hernias using mesh implants. Hernia 2001, no.5, p. 113-118), which could result in discomfort, inflammation andrecurrence of the hernia. Furthermore, permanently introducing a foreignmaterial into the human or animal body could be accompanied with sideeffects such as migration, chronic inflammation, risk of infection, etc.The introduction of a relatively large inert implant is also likely toinduce a long-term foreign body-reaction caused by the body's immunedefense system. As a result, the mesh implant may crumple up and loseits tissue supporting function.

A solution to this is described in U.S. Pat. No. 6,319,264 whichdescribes a porous, flexible and fibrous hernia mesh comprising twofunctional layers, wherein the first layer is a rapidly degradablepolymer layer facing the fascia, and wherein the second layer is a moreslowly degradable polymer layer. The mesh described in U.S. Pat. No.6,319,264 acts as a temporary support until connective scar tissue hasstrengthened enough and can replace the mesh, when the second layerfinally degrades. However, U.S. Pat. No. 6,319,264 is silent as to theload situation found over the tissue defect area and to any relatedadjustment of the relative distension of the hernia mesh.

Patent application EP 0797962 describes a mesh implant with a basicstructure made from a knitted fabric comprising non-resorbable materialor resorbable material, wherein the mesh is designed to stretch to allowmovement in the underlying tissue. To ease the procedure of cutting andhandling the mesh prior to insertion, the basic structure can bestrengthened by adding a stiffener. The stiffener comprises a resorbablematerial which is either coated onto the knitted fibers or supplied asfibers which are woven together with (i.e. in the same pattern as) thefibers of the basic structure. This stiffening material is designed toresorb soon after surgery. However, the mesh implant provided in patentapplication EP 0797962 offers no particular measures to facilitate theprimary formation of fibrotic tissue during the early stages of woundhealing.

The U.S. Patent Application No. 2006/0142786, which is assigned to thepresent assignee, describes a mesh implant of a resorbable polymercomprising at least two materials, wherein the second material issubstantially degraded at a later point in time than the first materialfollowing the time of implantation. The mesh implant is adapted to havea predetermined modulus of elasticity that gradually is decreased untilthe implant is completely degraded and subsequently absorbed. Due to thegradual decrease in the modulus of elasticity of the inventive meshimplant, the regenerating tissue may progressively take over the loadapplied to the tissue defect area. The U.S. Patent Application No.2006/0142786 describes using materials with different elasticityoverlaid on each other to achieve a gradual change in overall elasticityof the implant. To tailor for the properties of a mesh by choosingdifferent materials may, however, in the case of a resorbable mesh bedifficult, since the selection of suitable material commerciallyavailable is limited. In addition, these materials may be expensiveand/or difficult to handle during the manufacturing of the mesh. Theentire contents of U.S. Patent Application No. 2006/0142786 isincorporated herein by reference for the devices, techniques, andmethods disclosed therein.

Consequently, there is still a need for an improved mesh implant whichfacilitates the healing process by relieving the tissue during initialstages of healing and allows the regenerating tissue to gradually takeover the load during the progression of healing. It is therefore anobject of the present invention to provide such a mesh implant which iscompletely degradable.

SUMMARY OF THE INVENTION

The present invention provides a mesh implant with characteristicsallowing it to initially promote proper healing of the tissue lesion andthereafter gradually adjust to match conditions of the underlying tissuestructures of the human body, such as the abdominal wall. This isachieved in a first embodiment by constructing a mesh with two differentco-knitted materials with different degradation times relative to thetime of implantation.

The mesh implant comprises at least a first type of fibers and a secondtype of fibers knitted together in an interlocking manner, wherein thesecond type of fibers is substantially degraded at a later point in timethan the first type of fibers, following the time of implantation of themesh implant. The mesh implant is adapted to have a substantiallyconstant low relative distension during the primary wound healingperiod, after which period the relative distension is incrementallyincreased until the mesh implant substantially loses its mechanicalproperties and subsequently is completely degraded and absorbed by thebody. These changes in the relative distension of the mesh are achievedby using filamentous fibers that are knitted together such that thefilaments of the first set of fibers restrict the movement of the partof the mesh formed by the second set of fibers. When the first set offibers is degraded, the relative distension of the mesh implant issubstantially increased due to the fact that the movement of the part ofthe mesh formed by the second set of fibers is no longer constrained bythe first set of fibers. During the initial stages of healing, the meshrestricts the movement of the underlying tissue in order to facilitatethe primary steps in tissue regeneration. In addition, the porousstructure of the knitted mesh promotes the ingrowth of new tissue. Theregenerating tissue may thereafter gradually take over the load appliedto the tissue defect area, as a result of the gradual increase inflexibility of the inventive mesh implant, until the mesh implant iscompletely absorbed. With the inventive mesh implant there is no longera need for inert, non-resorbable, long-term supporting structures andthe risk of post-operative rupture or discomfort due to incompatibleelasticity of the mesh is minimized. In addition, the present inventioncan utilize known resorbable material or materials.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a first embodiment of the present invention, wherein themesh implant is comprised of two co-knitted sets of fibers A and B.

FIG. 2 shows the relative distension of the mesh implant shown in FIG. 1as a function of time (not to scale).

FIG. 3 shows the relative distension of a second embodiment of thepresent invention, wherein the mesh implant is comprised of threeco-knitted sets of fibers, C, D and E, as a function of time (not toscale).

FIG. 4 shows the relative distension of the two mesh implants describedin Example 1 as a function of time.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention is intended to be used in repair of soft tissue,i.e. tissue having some form of mobility and flexibility, including butnot limited to the abdominal wall, inner organs, aponeurotic structures,muscles, tendons, ligaments, but excluding e.g. bones and cartilage.

The present invention is based on the current knowledge that primarywound healing usually occurs over a time period of 2 to 14 days,followed by a remodeling period, which may extend up to and over 6months. The primary stage of wound healing is characterized by collagendeposition, granulation tissue formation and angiogenesis. During thisstage, it is desirable to minimize the movement within the wound area.Thereafter, during the remodeling period, the newly formed tissue willundergo several phases, during which the tissue gradually becomes morespecific to support the various stress situations found in the area. Theinventors of the present invention therefore suggest that a device usedto temporarily support the tissue defect in the area where the tissue isexposed to various stress situations should be so designed as to allowthe newly formed tissue to gradually take over the load during theremodeling phase and thus build up the strength and compliance needed totake over the full load once the support from the temporarily implanteddevice is lost.

Furthermore, gradually changing elasticity of the mesh implant should beachieved by using two or more filamentous materials, wherein thefilamentous fibers are knitted together. In addition, the filaments of afirst set of fibers are interlaced into the filaments of a second set offibers such that the filaments of the first set of fibers restrict themovement of the mesh formed by the second set of fibers.

FIG. 1 schematically shows a first embodiment of the present invention,wherein the mesh implant comprises two resorbable filamentous sets offibers, fibers A and fibers B. Fibers A are characterized by a time ofsubstantial degradation, t_(A). Consequently, fibers B are characterizedby a time of substantial degradation, t_(B). Fibers B are substantiallydegraded at a later point in time than fibers A, following the time ofimplantation of the mesh implant, i.e. t_(A)<t_(B). The time ofsubstantial degradation is herein defined as the point in time at whichthe material substantially loses its original integrity.

For the first embodiment of the present invention, t_(A) is in the timerange of 2 to 40 days, more preferably 5 to 30 days, or even morepreferably 10 to 20 days after the time of implantation, i.e. t=t₀, andt_(B) is at least 3-18 months after the time of implantation, preferablyin the time range of 6-12 months.

To achieve the gradual adjustment from promoting initial healing toconditions matching the underlying tissue structures of the wound site,an interlocking knit of the different fibers of the mesh implant isused, wherein the different fibers have different times of resorptionrelative to the time of implantation. The interlocking knit patterns canbe such that the first set of fibers at least partly traverses the poresformed by the second set of fibers (see FIG. 1) or even physicallybrings together (or close to one another) two or more points on thethreads of the second set of fibers, thereby restricting the overallsize of the pores in the mesh implant. The degradation of the first setof fibers allows increased pore size of the overall mesh, and therebypromotes further accumulation of extracellular matrix, fibroblasts, andother cells necessary for regeneration of the tissue. As mentioned, theincrease in pore size is due to an expansion or opening up of the knitpattern after degradation of the first set of fibers.

An elastic material is by definition a material that can stretch to acertain extent in response to a pulling or pushing force in at least onedirection and thereafter return to substantially its original shape andsize when released. Since the direction in which said force is appliedcan vary infinitely, elasticity of a material is a complex function. Onthe other hand, relative distension of a material, measured using a ballburst testing apparatus, is a definable characteristic. Here, thematerial is subjected to a steel ball exerting a pushing forceperpendicular to the plane of the flat material and the maximum lengththe ball can travel without failure of the material is used to calculaterelative distension. However, the term distension does not encompass theability of a material to return to its original size and shape.

As mentioned, the overall support characteristics of the mesh implantcan be measured as relative distension of the mesh using a ball bursttesting apparatus. The relative distension of a mesh, and in particularthe changes in the relative distension of the mesh according to thepresent invention over time after implantation into the body, isgoverned by two main factors, either separately or in combination. Thefirst factor, which has been touched upon above, is the change inrelative distension after degradation of one set of fibers resultingfrom the distortion or change of the overall mesh pattern itself, i.e. achange in relative distension which can occur even with fiberscomprising completely inelastic materials. To illustrate, even a meshmade of inelastic material, such as a common fishing net, exhibitsrelative distension when subjected to a force by increasing the porediameter in one dimension while decreasing the pore diameter in anotherdimension, i.e. distorting the shape of the pores. Therefore, since thefirst set of fibers initially lock the pattern of the second set offibers in the present mesh; degradation will lead to liberation of themesh formed by the second set of fibers alone which can result in ahigher overall relative distension of the mesh implant. The secondfactor affecting relative distension is the differences in inherentelasticity of the fiber materials themselves, depending on thecomposition of the materials used. In particular, the material of thefirst set of fibers can be less elastic than the material in the secondset of fibers, such that after degradation of the first material theoverall elasticity of the mesh is increased due to loss of the lesselastic first material. Therefore, the relative distension can be variedby using different materials and/or different knit patterns, whichprovides a wide range of possible scenarios for the change in relativedistension of the mesh implant over time.

FIG. 2 shows a schematic of the relative distension, RD, of the meshimplant shown in FIG. 1 as a function of time, t. Initially, untilt=t_(A), i.e. the time of substantial degradation for fibers A, therelative distension, RD₁, is essentially constant and preferably low,0-10%, more preferably 3-7%. The relative distension in this phase is aresult of the interlocking knitted structure of the two sets of fibers,as has been discussed above. At t=t_(A), the relative distension of themesh implant changes to a new, higher relative distension, RD₂, which isessentially solely dependent on the knit pattern and material of fibersB. Preferably, RD₂ is above 10%, more preferably 15-25%. Thus, RD₂corresponds to a relative distension of the mesh implant that approachesthe elasticity of the surrounding tissue, so that the flexibility ofsaid tissue is not substantially restricted, at least not for minormovement.

In a second embodiment of the inventive mesh implant a mesh implantcomprises three sets of fibers, C, D and E, each characterized by aspecific time of degradation, such that t_(C)<t_(D)<t_(E). FIG. 3 showsthe relative distension, RD, of such a mesh implant as a function oftime, t. In this embodiment, RD₃ is understood to be a function of theinterlocking knitted structure of the three sets of fibers, RD₄ afunction of the interlocking knitted structure of fibers D and E, and,consequently, RD₅ a function of the mesh structure solely formed byfibers E. Furthermore, RD₃<RD₄<RD₅, conferring a gradual increase in theoverall elasticity of the mesh implant. Thus, in the alternativeembodiment, the mesh implant comprises three sets of fibers C, D and E.This embodiment approximates more closely the ideal increase in RD (formany different types of tissues) of such a mesh implant, illustrated asa dotted line in FIGS. 2 and 3.

In the second embodiment, t_(C) is, comparable to t_(A) in the firstembodiment, in the time range of 2 to 40 days, more preferably 5 to 30days, or even more preferably 10 to 20 days after the time ofimplantation, with the intention that t_(C) is equivalent to the time ofinitial healing. Time t_(E) is at least 3-18 months after the time ofimplantation, preferably in the time range of 6-12 months. Time t_(D)can thus be anywhere between 2 days and 18 months, as long ast_(C)<t_(D)<t_(E).

Corresponding to the values of RD₁ and RD₂ in the first embodiment, RD₃,RD₄ and RD₅ should be evenly spread over the range of from 0% to 25-30%,where the latter value corresponds to the relative distension of theabdominal wall. RD₃ is preferably in the range of 0-10% or morepreferably 3-7%. RD₅ is preferably above 20%, more preferably in therange of 23-28%. RD₄ can thus be anywhere between 0% and approximately30%, as long as RD₃<RD₄<RD₅.

In other embodiments, the mesh implant according to the presentinvention can comprise four or five sets of fibers, taking intoconsideration the fact that each successive set of fibers increases themesh implant's approximation to the ideal increase in relativedistension of such a mesh implant, illustrated as a dotted line in FIGS.2 and 3.

It should be noted that the ability of a material to stretch in aparticular embodiment need not have the same value in all directions,thus the ability of a material to stretch in for instance one directionalong the plane of the mesh implant need not be identical to the abilityof a material to stretch in the perpendicular planar direction.Consequently, two embodiments can have the same relative distension(measured at an angle perpendicular to the plane of the mesh implant),but exhibit different abilities to stretch in different directions inthe plane of the mesh implant.

In the embodiments described above, the mesh implant can be fixed afterimplantation with for instance suitable sutures, staples, fixation,pins, adhesives or the like. In some applications of the implant, thepressure from the surrounding tissue may be enough for initial fixationuntil newly regenerating tissue anchors the implant by tissue throughgrowth.

During the described time of resorption for the overall mesh implant theload applied to the mesh will gradually be taken over by the surroundingand ingrowing tissue, due to the step-wise degradation of the differentsets of fibers, leading to increased compliance of the overall mesh.This allows a biomechanical stimulation of the tissue that will enableit to regenerate and remodel into a load-bearing tissue, e.g.aponeurotic structures, tendons or ligaments, which gradually will takeover the load carried by the mesh implant during the time period ofresorption.

The materials used to make the fibers used in the different embodimentsof the present invention can be any resorbable polymer, copolymer,polymer blend or polymer composite or other suitable material, or can becombined assorted resorbable polymer parts, as long as the materialshave suitable predetermined times of substantial degradation andelasticity, so that when the materials are combined, the inventive meshimplant imitates the ideal (for the particular tissue) relativedistension versus time situation of a resorbable mesh implant used totemporarily support soft tissue defects during reconstruction, asdescribed above. Non-limiting examples of such synthetic resorbablepolymers are made from the monomers glycolide, lactide and allstereoisomers thereof, trimethylene carbonate, e-caprolactone, dioxanoneor dioxepanone, or various combinations thereof. Depending on thedesired mechanical properties and the choice of manufacturing method,several of the homopolymers or copolymers containing two or more of theabove-mentioned monomers can be used to manufacture the mesh structure.Yet other examples of synthetic resorbable polymers that can be utilizedare various aliphatic polyurethanes, such as polyureaurethanes,polyesterurethanes and polycarbonateurethanes, and also materials suchas polyphosphazenes or polyorthoesters.

The type of knitting technique used to create the mesh implant of thepresent invention can be any type of knitting techniques, keeping inmind that the knit is constructed such that the overall relativedistension of the inventive mesh implant is stepwise increased at thetimes of degradation of each set of fibers. It is preferable that themesh implant is knitted using a technique that produces a mesh that isresistant to runs, such as a warp-knit procedure, to prevent tearing ofthe mesh during insertion or during the overall time of degradation ofthe mesh implant in the body.

The last substantially degraded material of the inventive mesh implant,preferably has a knitted structure with an aperture size preferably inthe range of 0.1-4.0 mm, more preferred 0.2-2.0 mm, in order to minimizethe mass of the mesh implant as well as maximizing the tissue supportingeffect of said last substantially degraded material.

It will be understood that the invention is not restricted to the abovedescribed exemplifying embodiments thereof and that many modificationsare conceivable. The changes in relative distension of the inventivemesh implant are further described in the following non-restrictiveexample.

EXAMPLE 1

The overall distension of the inventive mesh implant at 16 N/cm (see K.Junge et al.: Elasticity of the anterior abdominal wall and impact forreparation of incisional hernias using mesh implants. Hernia 2001, no.5, p. 113-118) for the ball burst testing apparatus was determined usingthe ASTM D3787-01 guideline for the fixture geometry (25.4 mm polishedsteel ball, 44.45 mm diameter inside opening). Two different meshes,knitted together in two different interlocking patterns, diamond patternand full-tricot, were tested. Both meshes were composed of the same twotypes of fibers. The fast degrading fiber (40% by weight) was atri-axial copolymer having a soft core and crystalline arms composed of86% glycolide, the rest being trimethylenecarbonate and lactide. Theslow degrading fiber (60% by weight) was a linear copolymer having asoft core and crystalline arms composed of 91.5% lactide, the rest beingtrimethylene carbonate. The area weight of each mesh was approximately135 g/m².

Samples of the mesh were immersed in phosphate buffer (pH 7.4) at 37degrees Celsius. The overall distension of the mesh was determined atdifferent time points. The mesh was clamped in the fixture without anyapplied tension and the ball was positioned in the center of the 44.45mm diameter opening. The ball was then brought down to a position on themesh such that a 0.1 N force was applied. The test was initiated and theball traveled at 2.54 cm/min until failure. For each test three piecesof data were recorded:

1) Maximum load obtained during the test (N)

2) The extension at the maximum load (mm)

3) The extension at 71 N load (mm)

The value of 71 N is derived from the diameter of the opening (4.445cm×16 N/cm=71 N). The extension at 71 N was used to determine therelative distension at 16 N/cm. The results are presented in FIG. 4.These results show that as the mesh decomposes over time the relativedistension increases as the first material is degraded.

Although the present invention has been described with reference tospecific embodiments, also illustrated by the drawings, it will beapparent for those skilled in the art that many variations andmodifications can be done within the scope of the invention as describedin the specification and defined with reference to the claims below. Themesh implant of the present invention has been described in the contextof repair of the abdominal wall. However, it should be noted that themesh implant can also be used as tissue support in other types ofsurgical procedures, such as wound healing of internal organs, muscles,tendons or other tissues. In addition, the mesh implant can be producedinto other shapes than a flat mesh, such as e.g. a pouch or a pocket tosupport an internal organ or other structure.

1. A resorbable polymeric mesh implant for use in reconstruction of softtissue defects, comprising: a first arrangement of resorbable materialcomprising fibers; and a second arrangement of resorbable materialcomprising fibers, the second arrangement of resorbable material beingsubstantially degradable at a later point in time than the firstarrangement of resorbable material, wherein the first arrangement ofresorbable material is in contact with the second arrangement ofresorbable material such that the first arrangement of resorbablematerial locks movement of the second arrangement of resorbable materialby traversing apertures of the second arrangement of resorbable materialto maintain relative distension of the mesh implant substantiallyconstant following a time of implantation and until the firstarrangement of resorbable material is substantially degraded, whereinafter the first arrangement of resorbable material is substantiallydegraded, the relative distension of the mesh implant substantiallyincreases, wherein the first arrangement of resorbable material issubstantially degraded at a point in time within a time range of 2-40days following implantation, and wherein the last substantially degradedarrangement of resorbable material is substantially degraded at a pointin time within a time range of 3-18 months following implantation.
 2. Aresorbable polymeric mesh implant for use in reconstruction of softtissue defects, wherein the mesh implant comprises: a first set ofresorbable polymeric fibers, and a second set of resorbable polymericfibers, wherein the fibers are knitted together, wherein filaments ofsaid first set of fibers are interlaced into filaments of the second setof fibers and at least partly traverse a knit pattern of the second setof fibers such that the filaments of the first set of fibers lock themovement of the part of the mesh implant formed by the second set offibers, and wherein the relative distension of the mesh implant issubstantially constant following the time of implantation and until saidfirst set of fibers is substantially degraded, and wherein the secondset of resorbable polymeric fibers is substantially degraded at a laterpoint in time than the first set of resorbable polymeric fibers, whereinthe first set of resorbable polymeric fibers is substantially degradedat a point in time within a time range of 2-40 days followingimplantation, and wherein the last substantially degraded set ofresorbable polymeric fibers is substantially degraded at a point in timewithin a time range of 3-18 months following implantation.
 3. Aresorbable polymeric mesh implant according to claim 2, wherein the meshimplant comprises a third set of fibers that is substantially degradedat a later point in time than the second set of fibers and the relativedistension of the mesh implant is substantially changed after the secondset of fibers is substantially degraded.
 4. A resorbable polymeric meshimplant according to claim 2, wherein the relative distension of themesh implant following the time of implantation and until said first setof fibers is substantially degraded is within the range of 0-10%.
 5. Aresorbable polymeric mesh implant according to claim 2, wherein therelative distension of the mesh implant following the time ofsubstantial degradation of the first set of fibers is above 10%.
 6. Aresorbable polymeric mesh implant according to claim 2, wherein thepolymeric mesh implant is a hernia mesh implant.
 7. A resorbablepolymeric mesh implant according to claim 2, wherein the mesh implantstretches more in one direction along the plane of the mesh implant thanin another direction along the plane of the mesh implant.
 8. Aresorbable polymeric mesh implant according to claim 2, wherein thepolymeric mesh implant is formed into a three-dimensional shape tosupport an internal body structure.
 9. A resorbable polymeric meshimplant according to claim 2, wherein the first set of fibers and/orfurther sets of fibers has or is incorporated into a knitted structurewith an aperture size in the range of 0.1-4.0 mm.
 10. A resorbablepolymeric mesh implant according to claim 2, wherein the mesh implant isknitted using a technique that produces a mesh that is resistant toruns.
 11. A method to repair a soft tissue defect, wherein a resorbablepolymeric mesh implant according to claim 1 is used.
 12. A resorbablepolymeric mesh implant according to claim 1, wherein the polymeric meshimplant is a hernia mesh implant.
 13. A resorbable polymeric meshimplant according to claim 1, wherein the mesh implant is fullyresorbable.
 14. A resorbable polymeric mesh implant according to claim2, wherein the mesh implant is fully resorbable.
 15. A resorbablepolymeric mesh implant according to claim 1, wherein the firstarrangement of resorbable material is substantially degraded at a pointin time within a time range of 5-30 days following implantation.
 16. Aresorbable polymeric mesh implant according to claim 2, wherein thefirst set of resorbable polymeric fibers is substantially degraded at apoint in time within a time range of 5-30 days following implantation.17. A resorbable polymeric mesh implant according to claim 1, whereinthe first arrangement of resorbable material is substantially degradedat a point in time within a time range of 10-20 days followingimplantation.
 18. A resorbable polymeric mesh implant according to claim2, wherein the first set of resorbable polymeric fibers is substantiallydegraded at a point in time within a time range of 10-20 days followingimplantation.
 19. A resorbable polymeric mesh implant according to claim1, wherein the second arrangement of resorbable material issubstantially degraded at a point in time within a time range of 6-12months following implantation.
 20. A resorbable polymeric mesh implantaccording to claim 2, wherein the second set of resorbable polymericfibers is substantially degraded at a point in time within a time rangeof 6-12 months following implantation.
 21. A resorbable polymeric meshimplant according to claim 1, wherein the relative distension of themesh implant following the time of implantation and until said firstarrangement of resorbable material is substantially degraded is withinthe range of 3-7%.
 22. A resorbable polymeric mesh implant according toclaim 2, wherein the relative distension of the mesh implant followingthe time of implantation and until said first set of fibers issubstantially degraded is within the range of 3-7%.
 23. A resorbablepolymeric mesh implant according to claim 1, wherein the relativedistension of the mesh implant following the substantial degradation ofthe first arrangement of resorbable material is within the range of15-25%.
 24. A resorbable polymeric mesh implant according to claim 2,wherein the relative distension of the mesh implant following thesubstantial degradation of the first set of fibers is within the rangeof 3-7%.
 25. A resorbable polymeric mesh implant according to claim 3,wherein a first relative distention of the mesh implant following thetime of implantation and until said first set of fibers is substantiallydegraded is within the range of 0-10%, a third relative distention ofthe mesh implant following the substantial degradation of the first setof fibers and substantial degradation of the second set of fibers isgreater than 20%, and a second relative distention of the mesh implantfollowing the substantial degradation of the first set of fibers butbefore the substantial degradation of the second set of fibers and thethird set of fibers is greater than the first relative distention of themesh implant and less than the third relative distention of the meshimplant.
 26. A resorbable polymeric mesh implant according to claim 1,wherein the last substantially degraded arrangement of fibers has aknitted structure with an aperture size in the range of 0.2-2.0 mm. 27.A resorbable polymeric mesh implant according to claim 2, wherein thelast substantially degraded set of resorbable polymeric fibers has aknitted structure with an aperture size in the range of 0.2-2.0 mm.